STUDI PENGARUH RASIO Co/Mo TERHADAP KARAKTER KATALIS CoMo/USY HASIL PREPARASI MENGGUNAKAN METODE KOIMPREGNASI

RIZA UMAMI NUR KHALIMAH
Jurusan Kimia. Fakultas Matematika dan Ilmu Pengetahuan Alam.
Universitas Sebelas Maret

Dipertahankan di depan Tim Penguji Skripsi pada :
Senin, 27 Januari 2014

Tim Penguji :
Dr. Eddy Heraldy, MSi
NIP. 19640305 200003 1002
Dr. Triana Kusumaningsih, S.Si,M.Si
NIP. 19730124 199903 2001

Pembimbing
Dr. Khoirina Dwi Nugrahaningtyas, M.Si
NIP. 19740419 200003 2001
Yuniawan Hidayat, S.Si., M.Si
NIP. 19790605 200501 1001



ABSTRAK

Telah dilakukan penelitian tentang preparasi katalis bimetal CoMo dengan pengemban Ultra Stable Zeolit (USY) menggunakan metode koimpregnasi. Tujuan dari penelitian ini adalah untuk mengetahui pengaruh rasio berat prekursor logam Co/Mo terhadap terhadap karakter katalis yang meliputi kristalinitas, kandungan logam total, keasaman total, luas permukaan, volume total pori dan rerata jejari pori.
Katalis dipreparasi dengan metode koimpregnasi dengan variasi rasio Co (2%, 4%, 6% dan 8%) b/b dan logam Mo 8% (b/b). Aktivasi katalis dengan kalsinasi gas N2 pada T = 550 °C selama 3 jam, oksidasi gas O2 pada T = 400 °C selama 2 jam dan reduksi gas H2 pada T = 400 °C selama 2 jam. Fasa dari material setelah koimpregnasi dikarakterisasi menggunakan difraksi sinar-X (XRD). Keasaman katalis dianalisis menggunakan FTIR dan metode gravimetri. Mineral yang ada dalam katalis dianalisis menggunakan XRF. Analisis dari permukaan katalis menggunakan Surface Area Analyzer (SAA).
Hasil penelitian menunjukkan perubahan intensitas dan pergeseran 2θ setelah pengembanan dengan XRD. Analisis XRF menunjukkan banyaknya logam yang teremban dalam katalis. Perubahan ikatan pada spektra terdeteksi dengan FTIR pada bilangan gelombang tertentu. Metode gravimetri menunjukkan keasaman total yang meningkat seiring dengan bertambahnya rasio Co/Mo. Hasil SAA menunjukkan luas permukaan tertinggi 536,9 m²/g, rerata jejari pori sebesar 19,068 Å dan volume total pori 0,4287 cc/g.

Kata kunci : karakterisasi katalis, katalis bimetal CoMo/USY, koimpregnasi.



STUDY ON THE EFFECT OF Co/Mo (b/b) RATIO IN CoMo/USY CATALYST CHARACTER
PREPARED USING COIMPREGNATION METHOD


RIZA UMAMI NUR KHALIMAH
Department of Chemistry, Faculty of Mathematic and Natural Science
Sebelas Maret University

ABSTRACT

A study of preparation CoMo bimetallic catalysts with supporting material Ultra Stable Y-Zeolite (USY) using coimpregnation method has been done. The purpose of this study was to determine the effect of metal precursor weight ratio of Co/Mo to the catalyst character include crystallinity, the total metal content, total acidity, surface area, total pore volume and average pore.
The catalysts were prepared by coimpregnation method with weight variation of metals Co (2% , 4% , 6% and 8%) w/w and metals Mo 8% (w/w). Activation of the catalyst by calcination N2 gas at T = 550 °C for 3 hours, the oxidation by O2 gas at T = 400 °C for 2 hours and the reduction by H2 gas at T = 400 °C for 2 hours. Phase of the material after coimpregnation was characterized using X-ray diffraction (XRD). The acidity of the catalyst was analyzed using FTIR and gravimetry method. Minerals present in the catalyst was analyzed using XRF. Surface of the catalyst using a Surface Area Analyzer (SAA) .
Increases of intensity and 2θ shifts after impregnation have been observed by XRD. XRF analysis shows percent metal coimpregnated in the catalyst. Bonding vibration changes in the FTIR spectra detected at a particular wave number. Increasing total acidity due the higher ratio of Co/Mo observed by gravimetry method. SAA results showed the highest surface area is ​​536.9 m²/g, average pore 19.068 Å and total pore volume 0.4287 cc/g.

Keywords : characterization of the catalyst, the bimetallic catalysts CoMo/USY, coimpregnation


-------------------